Residual porosity at the surface of a hot isostatically pressed beta alumina tube (TM-MS-051)

It has always been found that a beta alumina tube which had been subjected to a post firing hot isostatic pressing cycle has a surface layer of enhanced porosity which is of the order of 100µ m thick. May has suggested that this is due to access of the pressuring...